Chemical Composition
Copper 84% - 86%, Tin 4% - 6%, Lead 4% - 6%, Zinc 4% - 6%
Tensile Strength 30000 LBS, Yeild 14000 LBS, Elongation 20%, Brinell Hardness 55-65, Pouring Temperature 1950F - 2350F
Chemical Composition
Copper 78% - 82%, Tin 2.5% - 3.5%, Lead 6.3% - 7.7%, Zinc 7% - 10%
Tensile Strength 29000 LBS, Yeild 13000 LBS, Elongation 18%, Brinell Hardness 50-60, Pouring Temperature 1950F - 2300F
Chemical Composition
Copper 88% - 90%, Tin 10% - 12%
Tensile Strength 35000 LBS, Yeild 18000 LBS, Elongation 10%, Pouring Temperature 1800F - 2000F
Chemical Composition
Copper 86% - 88.5%, Tin 9.3% - 10.5%, Lead .8% - 1.2%, Zinc 1.25% - 2.5%
Tensile Strength 35000 LBS, Yeild 18000 LBS, Elongation 10%, Brinell Hardness 65-80, Pouring Temperature 1920F - 2300F
Chemical Composition
Copper 86% - 89%, Tin 7.5% - 9%, Zinc 3% - 5%
Tensile Strength 40000 LBS, Yeild 18000 LBS, Elongation 20%, Brinell Hardness 60-75, Pouring Temperature 1900F - 2300F
Chemical Composition
Copper 86% - 90%, Tin 5.5% - 6.5%, Lead 1% - 2%, Zinc 3% - 5%
Tensile Strength 34000 LBS, Yeild 16000 LBS, Elongation 22%, Brinell Hardness 60-72, Pouring Temperature 1900F - 2300F
Chemical Composition
Copper 81% - 85%, Tin 6.5% - 7.5%, Lead 6% - 8%, Zinc 2% - 4%
Tensile Strength 30000 LBS, Yeild 14000 LBS, Elongation 15%, Brinell Hardness 55-65, Pouring Temperature 1950F - 2350F
Chemical Composition
Copper 55% - 60%, Tin 1%, Zinc Remainder
Tensile Strength 65000 LBS, Yeild 25000 LBS, Elongation 20%, Brinell Hardness 90-120, Pouring Temperature 1700F - 2050F
Chemical Composition
Copper 3% - 4%, Iron 1%, Silcon 5.5% - 6.5%, Zinc 1%, Aluminum Remainder
Tensile Strength 23000 LBS, Yeild 13000 LBS, Elongation 2.5%, Brinell Hardness 70, Pouring Temperature 1175F - 1450F
Chemical Composition
Silcon 6.5% - 7.5%, Zinc 1%, Aluminum Remainder
Tensile Strength 25000 LBS, Yeild 20000 LBS, Elongation 3%, Brinell Hardness 70, Pouring Temperature 1250F - 1450F
Chemical Composition
Copper .4% - 1%, Iron 1.1%, Zinc 7% - 8%, Aluminum Remainder
Tensile Strength 32000 LBS, Yeild 22000 LBS, Elongation 3%, Brinell Hardness 75, Pouring Temperature 1250F - 1450F